Part Details | POLYURETHANE COATING
8010-01-480-2610 A coating material in which the basic film-forming component is polyurethane, oil modified polyurethane, or resin modified polyurethane. It may be pigmented.
Alternate Parts: HMS151135*T1, HMS15-1135*T1, HMS151135*T1, HMS15-1135*T1, 8010-01-480-2610, 01-480-2610, 8010014802610, 014802610
| Supply Group (FSG) | NSN Assigned | NIIN | Item Name Code (INC) |
|---|---|---|---|
| 80 | NOV 13, 2000 | 01-480-2610 | 29027 ( POLYURETHANE COATING ) |
REFERENCE DRAWINGS & PICTURES
Cross Reference | NSN 8010-01-480-2610
| Part Number | Cage Code | Manufacturer |
|---|---|---|
| HMS15-1135*T1 | 8V613 | BOEING COMPANY, THEDBA BOEING |
| HMS15-1135*T1 | 02731 | MCDONNELL DOUGLAS HELICOPTER CO INC |
Technical Data | NSN 8010-01-480-2610
| Characteristic | Specifications |
|---|---|
| APPLICATION METHOD | L$DAM$N |
| SPECIAL FEATURES | USED FOR CONFORMAL COATING APPLICATION; GENERAL APPLICATION; STORAGE LIFE STORAGE IN THE ORIGINAL UNOPENED COTAINER AT TEMPERATURES BETWEEN 40 DEG AND 90 DEG F FOR A MINIMUM OF 12 MONTHS; THE VISCOSITY OF THE COATING MATERIAL AFTER COMBINING AND MIXING THE TWO COMPONENTS SHALL BE FROM 18 TO 20 SECONDS |
| SUPPLEMENTARY FEATURES | THE CURED COATING SHALL BE RESISTANT TO FINGERNAIL SCRAPING; ADEQUATE VENTILATION SHOULD BE USED IN THE AREA OF ITS USAGE; SKIN CONTACT WITH THE MATERIAL MAY CAUSE SKIN SENSITIZATION; MAINTAIN MIXTURE AT 24 DEG PORM 3 DEG CDURING TESTING |
| END ITEM IDENTIFICATION | HP10-7 HELICOPTER |
| PART NAME ASSIGNED BY CONTROLLING AGENCY | COATING, POLTURETHANE, CONFORMAL |